Grade:VF710
Product: High Adhesion Middle Temperature Hot Melt Adhesive Resin 110℃
Descriptions
VF710 is a maleic anhydride and vinyl acetate functionalized polyethylene mixture, easy to form film, with excellent processability and adhesive strength.
Raw Materials Used in Hot Melt Adhesives
The raw materials in a hot melt affect its cost, performance, function, and availability. Generally, the hot melt is made up of a polymer and many additives that can come in various forms. Some of these additives are antioxidants, resins, plasticizers, and waxes. Other chemicals can be added to give the hot melt more properties.
Physical Properties
|
Properties
|
Standard
|
Test Condition
|
Units
|
Typical Value
|
|
Density
|
ASTM D1505
|
23℃
|
g/cm3
|
0.94
|
| MFR |
ASTM D1238
|
190℃,2.16 kg
|
g/10min
|
3.0
|
|
Shore Hardness
|
ASTM D2240
|
Shore D
|
— |
45
|
Mechanical Properties
| Properties |
Standard |
Test Condition |
Units |
Typical Value |
| Tensile Yield Strength |
ASTM D638 |
100mm/min |
Mpa |
6.2 |
| Tensile Breaking Strength |
ASTM D638 |
100mm/min |
Mpa |
18.4 |
| Elongation at Break |
ASTM D638 |
100mm/min |
% |
＞750
|
Thermal Properties
| Properties |
Standard |
Test Condition |
Units |
Typical Value |
|
Melting Point
|
ASTM D3418
|
10℃/min
|
℃
|
105
|
|
VSP
|
ASTM D1525
|
2℃/min
|
℃
|
80
|
Note:The datas is used for referential purpose only, not for quality commitment.
Advantages
- Good film forming performance, can be formed into 0.02 ㎜ thick film;
- High adhesive strength, good durability, excellent adhesive interface performance, showing the interface adhesive cohesion energy destruction;
- Can withstand a certain acid, alkali, salt spray and other chemical solvent corrosion;
- Strong adaptability, can meet the needs of high-speed production;
- Good weather resistance, adapt to the climate temperature change environment, can be outdoor use.
Chemical Structure
Composition: Maleic Anhydride and Vinyl Acetate functionalized polyethylene mixture.
Application
VF710 is widely used as binder for aluminum plastic panel and heat insulation panel.
Recommended Processing Technology.
Zone 1 Temperature 125~135 ℃
Zone 2 Temperature 135~145 ℃
Zone 3 Temperature 145~155 ℃
Zone 4 Temperature 145~155 ℃
Die Temperature 155~165 ℃
Melt Temperature ＜230℃
Statement: the above processing technology shall be different according to different conditions such as product size, mold design and processing equipment specification, and the details shall be adjusted according to the actual situation.